HOT WORK TOOL STEELS
| DIN NORMAL | ALLOY ELEMENTS % | Other Brands | Softening Annealing Degree (°C) | Hardness after Soft Annealing (HB) | |||||||
| NS | NS | mn | cr | B.C | Ni | V | W | ||||
| 1.2581 x30WCRv93 | 0.29 | 0.25 | 0.30 | 2.7 | - | - | 0.35 | 8.5 | -H21 | 750-800 | Max 240 |
| 1.2344 x40CRMoV51 | 0.39 | 1.00 | 0.40 | 5.1 | 1.30 | - | 1.00 | - | -H13 ORVAR 2M | 750-800 | Max 229 |
| 1.2367 X38CRMoV 5-3 | 0.38 | 0.40 | 0.40 | 5.0 | 2.8 | - | 0.65 | - | - | 750-800 | Max 229 |
| 1,2365 X323CR MoV 33 | 0.31 | 0.30 | 0.35 | 2.9 | 2.8 | - | 0.50 | - | -H10 | 750-800 | Max 229 |
| 1,22714 56 NICR MoV7 | 0.55 | 0.25 | 0.75 | 1.1 | 0.50 | 1.7 | 0.10 | - | -L6 ALVAR | 650-700 | Max 248 |
| DIN Norm | Stress Retention Degree (°C) | Hardening Degree (°C) | Hardening Means | Hardness After Hardening (HRC) | Hardness after tempering (HRC) | |||
| 400°C | 500°C | 600°C | 700°C | |||||
| 1.2581 x30 WCr V93 | 600-650 | 1070-1150 | YSB | 48-52 | 50 | 51 | 50 | 38 |
| H | 44-48 | |||||||
| 1.2344 x 40 Cr Mo u 51 | 600-650 | 1020-1080 | YSB | 52-56 | 53 | 54 | 48 | 30 |
| H | 50-54 | |||||||
| 1.2367 x 38 Cr Mo V 33 | 600-650 | 1030-1080 | YSB | 52-56 | 52 | 54 | 50 | 35 |
| H | 50-54 | |||||||
| 1,2365 x 32 Cr Mo V 33 | 600-650 | 1010-1050 | YSB | 52-56 | 50 | 51 | 50 | 36 |
| H | ||||||||
| 1.2714 x 56NiCrMoV 7 | 650-700 | 830-870 | Y | 52-58 | 48 | 46 | 40 | - |
| 870-900 | H | 44-50 |
| DIN NORMAL | usage areas |
| 1.2581 x30 WCr V93 | This steel, which has a very high strength resistance, is used in forging and coating works of materials to be shaped at high temperatures. |
| 1.2344 x40 Cr Mou V51 | Iron-Steel profile pressing tools, main mold core and punching punches for fringe forming of aluminum and alloys |
| 1.2367 x 38 Cr Mo V 33 | In the manufacture of water-cooling press punch press die hot flow press die hot cutting blades screw nut rivets for mineral pipe and bar drawing press |
| 1,2365 x 32 Cr Mo V 33 | Hot cutting shear blades as they are resistant to constant temperature change in hot forming of copper-brass and bronzes |
| 1.2714 56 NiCrMo V 2 | In the manufacture of iron-steel and forging dies |